Wax decoration items and method making the same

ABSTRACT

A wax decoration item is made by the method including the steps of mixing preparing polyethylene wax, cyanide polymer and white wax to be a mixture by way of heating; pouring the mixture in a mold and obtaining a wax item with fixed shape when removing the mold; melting a colloid material to be a transparent liquid and coating the colloid material onto an outer periphery surface of the wax item and the colloid material being not mixed with the wax item; condensing the colloid material which is fixed on the wax item.

FIELD OF THE INVENTION

[0001] The present invention relates to a wax decoration item and amethod for making the item wherein the item has a colloid outer layerwhich is not mixed with the wax of the decoration item.

BACKGROUND OF THE INVENTION

[0002] A conventional way to make a wax decoration item 51 in a colloiditem 50 as shown in FIG. 1 has an inherent problem which is that thepigment for the wax decoration item 51 will be mixed with the colloiditem 50. A mixture area 52 is presented around the wax decoration item51. The other problem of the conventional way is shown in FIG. 2 and theproblem is that the surface 53 of the wax decoration item 51 is meltedso that the shape and color of the wax decoration item 51 cannot besharply and precisely presented.

[0003] The present invention intends to provide a wax decoration itemand a method for making the same. The was decoration item includes acolloid outer layer on the wax decoration item so as the present thedesired shape of the wax decoration item.

SUMMARY OF THE INVENTION

[0004] In accordance with one aspect of the present invention, there isprovided a method for making a wax decoration item and the methodcomprises the following steps:

[0005] step 1: preparing polyethylene wax, cyanide polymer and whitewax;

[0006] step 2: mixing the polyethylene wax, cyanide polymer and whitewax to be a mixture by way of heating;

[0007] step 3: pouring the mixture in a mold and obtaining a wax itemwith fixed shape when removing the mold;

[0008] step 4: melting a colloid material to be a transparent liquid;

[0009] step 5: coating the colloid material onto an outer peripherysurface of the wax item and the colloid material being not mixed withthe wax item, and

[0010] step 6: condensing the colloid material which is fixed on the waxitem.

[0011] The primary object of the present invention is to provide amethod for making a wax decoration item wherein the colloid materialfixed on the outer surface of the wax item is not mixed with the waxitem.

[0012] The present invention will become more obvious from the followingdescription when taken in connection with the accompanying drawingswhich show, for purposes of illustration only, a preferred embodiment inaccordance with the present invention.

BRIEF DESCRIPTION OF THE DRAWINGS

[0013]FIG. 1 is a perspective view to show a conventional way to make awax decoration item;

[0014]FIG. 2 is a perspective view to show another conventional way tomake a wax decoration item;

[0015]FIG. 3 is a flow chart to show the steps of the method of thepresent invention;

[0016]FIGS. 4 and 5 are a perspective view to show the wax decorationitems of the present invention can be made to be different shapes;

[0017]FIG. 6 is a perspective view to show a wick is connected to thewax decoration item of the present invention, and

[0018]FIG. 7 shows a film is put in the inside of the mold and the waxdecoration item of the present invention is put in the mold.

DETAILED DESCRIPTION OF THE INVENTION

[0019] Referring to FIG. 3, the method for making a wax decoration itemof the present invention comprises the following steps:

[0020] step 1: preparing polyethylene wax, cyanide polymer and whitewax;

[0021] step 2: mixing the polyethylene wax, cyanide polymer and whitewax to be a mixture by heating them;

[0022] step 3: pouring the mixture in a mold and obtaining a wax item 10with fixed shape when removing the mold 30;

[0023] step 4: melting a colloid material 20 to be a transparent liquid;

[0024] step 5: coating the colloid material 20 onto an outer peripherysurface of the wax item 10 and the colloid material 20 being not mixedwith the wax item 10, and

[0025] step 6: condensing the colloid material 20 which is fixed on thewax item 10.

[0026] The melting temperature and the condensing temperature of thecolloid material 20 are lower than those of the wax item 10. The weightratio between the polyethylene wax, the cyanide polymer and the whitewax in steps 1 and 2 is 3-6%:7-11%:85-88%. The melting temperature andthe condensing temperature are located in a range of 80-170 degreesCelsius. The preferred weight ratio between the polyethylene wax, thecyanide polymer and the white wax in steps 1 and 2 is 4.5%:9%:86.5%, themelting temperature and the condensing temperature being 125 degreesCelsius.

[0027] The shape of the wax decoration items 10 in step 3 can bedifferent such as flowers as shown in FIG. 4 and fruits as shown in FIG.5.

[0028] The colloid material 20 in step 4 is a mixture of the cyanidepolymer and the white wax, and the weight ratio between the cyanidepolymer and the white wax is 7-11%:89-93%. The melting temperature andthe condensing temperature are located in a range of 75-140 degreesCelsius. The preferred weight ratio between the cyanide polymer and thewhite wax is 9%:91%, and the melting temperature and the condensingtemperature are 120 degrees Celsius.

[0029] It is to be noted that inorganic pigment can be added in themixture of the polyethylene wax, the cyanide polymer and the white waxin step 1 or 2. Also. The inorganic pigment can be added in the colloidmaterial in step 4. Fragrance is added in the mixture in either step 1or step 2. The fragrance can also be added in the colloid material 20 instep 4.

[0030] As shown in FIG. 6, the wax decoration item 10 may also be madeto be a candle wherein a wick 40 is put in the wax item 10 in step 5 andthe wick 40 extends out from the colloid material 20.

[0031] Referring to FIG. 7, a film 32 is put in an inside of a mold 31in step 5 and the wax item 10 is put in the mold 31. The film 32 ispeeled from the colloid material 20 after the colloid-material 20 iscooled.

[0032] The colloid material 20 of the present invention will not mixwith the outer surface of the wax decoration item 10 so that the shapeof the wax decoration item 10 is sharp and precise.

[0033] While we have shown and described the embodiment in accordancewith the present invention, it should be clear to those skilled in theart that further embodiments may be made without departing from thescope of the present invention.

What is claimed is:
 1. A method for making a wax decoration itemcomprising the following steps: step 1: preparing polyethylene wax,cyanide polymer and white wax; step 2: mixing the polyethylene wax,cyanide polymer and white wax to be a mixture by way of heating; step 3:pouring the mixture a mold and obtaining a wax item with fixed shapewhen removing the mold; step 4: melting a colloid material to be atransparent liquid; step 5: coating the colloid material onto an outerperiphery surface of the wax item and the colloid material being notmixed with the wax item, and step 6: condensing the colloid materialwhich is fixed on the wax item.
 2. The method as claimed in claim 1,wherein the melting temperature and the condensing temperature of thecolloid material are lower than those of the wax item.
 3. The method asclaimed in claim 1, wherein the weight ratio between the polyethylenewax, the cyanide polymer and the white wax in steps 1 and 2 is13-6%:7-11%:85-88%, the melting temperature and the condensingtemperature located in a range of 80-170 degrees Celsius.
 4. The methodas claimed in claim 1 or 3, wherein the preferred weight ratio betweenthe polyethylene wax, the cyanide polymer and the white wax in steps 1and 2 is 4.5%:9%:86.5%, the melting temperature and the condensingtemperature being 125 degrees Celsius.
 5. The method as claimed in claim1, wherein the colloid material in step 4 is a mixture of the cyanidepolymer and the white wax, the weight ratio between the cyanide polymerand the white wax is 7-11%:89-93%, the melting temper and the condensingtemperature located in a range of 75-140 degrees Celsius.
 6. The methodas claimed in claim 1 or 5, wherein the colloid material in step 4 is amixture of the cyanide polymer and the white wax, the preferred weightratio between the cyanide polymer and the white wax is 9%:91%, themelting temperature and the condensing temperate being 120 degreesCelsius.
 7. The method as claimed in claim 1, further comprisinginorganic pigment added in the mixture of the polyethylene wax, thecyanide polymer and the white wax in step
 1. 8. The method as claimed inclaim 1, further comprising inorganic pigment added in the mixture ofthe polyethylene wax, the cyanide polymer and the white wax in step 2.9. The method as claimed in claim 1, further comprising inorganicpigment added in the colloid material in step
 4. 10. The method asclaimed in claim 1, further comprising fragrance added in the mixture ineither step 1 or step
 2. 11. The method as claimed in claim 1, furthercomprising lance added in the colloid material in step
 4. 12. The methodas claimed in claim 1, further comprising a film being put in an insideof a mold in step 5 and the wax item being put in the mold, the filmbeing peeled from the colloid material after the colloid material beingcooled.
 13. The method as claimed in claim 1, the comprising a wick inthe wax item in step 5 and the wick extending out from the colloidmaterial.
 14. A wax decoration item comprising a mixture of polyethylenewax, cyanide polymer and white wax.
 15. The wax decoration item asclaimed in claim 14, wherein the weight ratio between the polyethylenewax, the cyanide polymer and the white wax is 3-6%:7-11%:85-88%, themelting temperature and the condensing temperate located in a range of80-170 degrees Celsius.
 16. The wax decoration item as claimed in claim14, wherein the preferred weight ratio between the polyethylene wax, thecyanide polymer and the white wax is 4.5%:9%:86.5%, the meltingtemperature and the condensing temperature being 125 degrees Celsius.17. The wax decoration item as claimed in claim 14, wherein a colloidmaterial is coated to the wax decoration item and the meltingtemperature and the condensing temperature of the colloid material arelower than those of the wax decoration item.
 18. The wax decoration itemas claim in claim 17, wherein the colloid material is a mixture of thecyanide polymer and the white wax, the weight ratio between the cyanidepolymer and the white wax is 7-11%:89-93%, the melting temperature andthe condensing temperature located in a range of 75-140 degrees Celsius.19. The wax decoration item as claimed in claim 17, wherein the colloidmaterial in step 4 is a mixture of the cyanide polymer and the whitewax, the preferred weight ratio between the cyanide polymer and thewhite wax is 9%:91%, the melting temperature and the condensingtemperature being 120 degrees Celsius.
 20. The wax decoration item asclaimed in claim 14, further comprising inorganic pigment added in themixture of the polyethylene wax, the cyanide polymer and the white wax.21. The wax decoration item as claimed in claim 14, further comprisinginorganic pigment added in the colloid material.
 22. The wax decorationitem as claimed in claim 14, further comprising fragrance added in themixture of the polyethylene wax, the cyanide polymer and the white wax.23. The wax decoration item as claimed in claim 14, further comprisingfragrance added in the colloid material.
 24. The wax decoration item asclaimed in claim 14, further comprising a wick in the mixture of thepolyethylene wax, the cyanide polymer and the white wax, the wickextending out from the colloid material.